Synthesis and Characterization of Lanthanum doped Co-Zn Spinel Ferrites Nanoparticles by Sol-Gel Auto Combustion Method
ISSN: 2791 - 0601
Publisher: author
Synthesis and Characterization of Lanthanum doped Co-Zn Spinel Ferrites Nanoparticles by Sol-Gel Auto Combustion Method
Indexed in
Physics and Astronomy
ARTICLE-FACTOR
1.3
Article Basics Score: 2
Article Transparency Score: 2
Article Operation Score: 3
Article Articles Score: 3
Article Accessibility Score: 2
SUBMIT PAPER ASK QUESTION
International Category Code (ICC):
ICC-1302
Publisher: International Research Alliance For Sustainable Development
International Journal Address (IAA):
IAA.ZONE/2791384670601
eISSN
:
2791 - 0601
VALID
ISSN Validator
Abstract
Spinel ferrites nanoparticles play a significant role in our everyday lives. In the current work, La3+ doped Co-Zn ferrites with chemical formula Co0.5Zn0.5LaxFe2-xO4 (x = 0.00 to x = 0.2 with step size 0.04) was effectively prepared by sol gel technique. The formation of FCC spinel structure was confirmed by X-Ray diffraction (XRD) analysis. The average crystallite size were calculated to be in the 8 nm to 13 nm range. The lattice parameters were found to be decreased with the doping of lanthanum (La3+) contents. X- Ray density is analyzed to increase as the concentration of (La3+) doping increases, this is due to the fact that La3+ ion has a higher molar weight than Fe3+ ion. The spinel phase structure was affirmed by using FTIR.The two main absorption bands ?1 and ?2 are referred to tetrahedral stretching band and octahedral stretching band respectively, is found to be in the range of at around 400-530 cm-1. Spinel ferrites, such a...